Effects of rare earth elements and antimony on morphology of spheroidal graphite in heavy-walled ductile cast iron
Auteur(s)
TSUMURA O. ; ICHINOMIYA Y. ; NARITA H. ; ...
Résumé
It is well known that the mechanical properties of heavy-walled ductile cast iron decrease due to morphological changes of spheroidal graphite. The effects of RE and Sb contents on the morphological changes of graphite (especially the appearance of chunky graphite and exploded graphite) were studied using a test block which was solidified with the simulated time for heavy-walled ductile casting. The followings were confirmed in this study. (1) Exploded graphite appears when RE contents are above 0.02 mass % (2) Chunky graphite does not appear when the Sb/RE ratio is above 0.7. The cause of the chunky graphite appearance will be studied next.
Editeur
Nippon Imono Kyokai
Identifiant
ISSN : 0021-4396 CODEN : IMNOA9
Source
Imono A. 1995, vol. 67, n° 8, pp. 540-545 [bibl. : 21 ref.]
Langue
Japonais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :