Comportement et durée de vie en fatigue isotherme de l'acier X 38 CrMoV 5
Isothermal fatigue beha viour and lifetime of a 5 % Cr hot work tool steel
Auteur(s)
DELAGNES D. ; REZAÏ-ARIA F. ; LEVAILLANT C. ; ...
Corporation(s) du ou des auteurs
Cercle d'études des métaux Saint-Etienne FRA (Commanditaire)
Résumé
Dies and molds are subjected to severe mechanical and thermal loads during injection or forging operations, As fatigue is one of the most important cause of tool steels damage, we studied isothermal (between 200°C and 600°C) fatigue behaviour and damage of two grades (SMV3 and ADC3) of a tempered martensitic 5 % Cr steel. More than 100 fatigue tests were performed in order to analyse mechanical loading, temperature and initial hardness influences. We observed a softening during all lifetime which is typical of tempered martensitic steels Softening amplitudes are increasing with increasing total strain amplitude, and decreasing with increasing temperature (till 550°C) and hardness (between 42 HRC and 50 HRC). Influences of temperature and hardness are limited when observed through a Manson-Coffin diagram, Conversely, increasing test temperature or decreasing hardness leads to a strong reduction of lifetime (factor 1000 for a 8 HRC decrease!) when results are plotted in a Basquin diagram. Interrupted tests showed that crack initiation controls lifetime for a number of cycles to failure around 105 cycles. Three sites of crack initiation were identified and discussed. - non metallic inclusions (200°C-400°C); - lath boundary (200°C-400°C), - prior austenitic grain boundary (500°C-600°C).
Editeur
EDP Sciences
Type du document
Conférence : Cercle d'Etudes des Métaux. Colloque, Albi, FRA, 1998-05-27
Identifiant
ISSN : 0032-6895 CODEN : MATCBW
Source
Matériaux et techniques A. 1999, vol. 87, n° 1-2, pp. 39-50 [bibl. : 27 ref.]
Langue
Français
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :