Dense manganese zinc ferrites and lead lanthanum zirconate titanate ceramics with fine grains
Auteur(s)
TOYOTA S. ; MIYOSHI Y. ; TAKATA M.
Résumé
Dense manganese zinc ferrites (MnZn ferrites) and lead lanthanum zirconate titanate (PLZT) with fine grains were fabricated by post-hot isostatic pressing (HIP) technique using finely ground starting powders prepared by a media agitation milling method. The average particle size of MnZn ferrites milled by media agitation milling was 0.03 μm, and the average grain size of the HIP'ed body was 1.2 μm. The ferrites showed low power-loss at high frequencies and initial permeability of 500 at 10 MHz. HIPing treatment of PLZT ceramics improved the transmittance without significant increase in grain size. The optical transmittance and grain size of HIP'ed PLZT were 69% at the wavelength of 750 nm and 2 μm, respectively. PLZT with fine grains showed microscopically uniform birefringence (...)
Editeur
Society of Materials Science
Identifiant
ISSN : 0514-5163 CODEN : ZARYAQ
Source
Zairyo A. 1994, vol. 43, n° 492, pp. 1047-1052 [bibl. : 8 ref.]
Langue
Japonais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :