Sintering of β tirtanium : role of dislocation pipe diffusion
Auteur(s)
SUNDARESAN R. ; RAGHURAM A. C. ; MALLYA R. M. ; ...
Résumé
Sintering of titanium in its high temperature β phase was studied by isothermal dilatometry. The sintering shrinkage y did not follow the normal time exponent type of behaviour, instead being described by the equation y = Ktm/[1 - (A + Bt)2], where m=1.93±0.07, with an activation energy of 62-90 kJ mol-1. A detailed analysis of these results, based on the 'anomalous' diffusion behaviour reported for β titanium, is carried out. It is shown that the generation of a high density of dislocations during the α→β phase transformation, coupled with sluggish recovery at the sintering necks, enables sintering mass transport by pipe diffusion through dislocation cores from sources of matter within the particles to become dominant.
Editeur
Maney
Identifiant
ISSN : 0032-5899 CODEN : PWMTAU
Source
Powder metallurgy A. 1996, vol. 39, n° 2, pp. 138-142 [bibl. : 42 ref.]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :