Détail de la notice
Titre du Document
Dislocations in Fe-45 at.% Al + B after high-temperature deformation
Auteur(s)
MUNROE P. R. ; BAKER I.
Résumé
The dislocation structures of large-grained low-temperature-annealed Fe-45at.%Al+B specimens strained to failure over the temperature range 400-1000K have been investigated using transmission electron microscopy. Up to and including 700 K, only <111> slip was observed but, in specimens strained at 800 K and above, both <111> and <001> slip were observed. The onset of <001> slip at 800 K coincides with the temperature at which a peak in the yield stress occurs in this alloy as shown by Klein and Baker in 1994. Optical metallography showed no evidence of either grain-boundary migration or dynamic recrystallization but, at 1000K, both static recrystallization and significant cavitation were noted. Cavitation is a feature common to solute-containing alloys.
Editeur
Taylor & Francis
Identifiant
ISSN : 1364-2804
Source
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :