Microstructural characterization of rapidly solidified ultrahigh boron tool steels
Auteur(s)
JIMENEZ J. A. ; ADEVA P. ; FROMMEYER G. ; ...
Résumé
Argon atomized powders of two modified boron-containing-tool steels in the rapid solidification condition as well as the consolidated materials after hot isostatic pressing at different temperatures were investigated. The microstructure of the powders of both tool steels consists of primary dendrites of solidification and a network of the M23(B,C)6 borocarbide forming a continuous phase. The metastable M3B boride is present because of the high solidification rates involved in the atomization process. This microstructure is gradually lost when the temperature of consolidation by hot isostatic pressing is increased. A fine and uniform microstructure is developed after consolidation at 1100 °C. An increase of hardness with an increase of consolidation temperature is observed which is associated to the presence of martensite since both alloys have a composition characteristic of air-hardening steels. After two consecutive tempering treatments at 650°C for 2h the martensite is decomposed and a decrease of hardness with increasing consolidation temperature is observed.
Editeur
Hanser
Identifiant
ISSN : 0044-3093 CODEN : ZEMTAE
Source
Zeitschrift für Metallkunde A. 1995, vol. 86, n° 10, pp. 693-699 [bibl. : 14 ref.]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :