Influence of volume fraction of martensite on the work hardening behaviour of two dual-phase steels with high and low silicon contents
Auteur(s)
NOURI Ashkan ; SAGHAFIAN Hasan ; KHEIRANDISH Shahram
Résumé
Two low carbon steels with the same manganese content (approximately 1.6 wt.%) but different silicon contents (0.34 and 2.26 wt.%) with the initial microstructures consisting of ferrite and pearlite were intercritically annealed at five different temperatures followed by water quenching to obtain dual-phase microstructures. The modified Crussard-Jaoul analysis was employed to describe the work hardening behaviour of the dual-phase steels. Both steels exhibited two stages of work hardening in the range of plastic deformation. It is shown that for each stage the work hardening exponent is not constant and varies with volume fraction of martensite and silicon content. The dependence of the transition stress σk and strain εk of dual-phase steels on the annealing temperature is discussed for both steels. It is concluded that εk increases with increasing silicon content and decreases with annealing temperature, while the reverse is true for σk.
Editeur
Hanser
Identifiant
ISSN : 1862-5282
Source
International journal of materials research A. 2010, vol. 101, n° 10, pp. 1286-1292 [7 pages] [bibl. : 46 ref.]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :