Characterization of Anode.Supported Solid Oxide Fuel Cells With Nd2Ni04 Cathodes
Auteur(s)
HAANAPPEL V. A. C. ; LALANNE C. ; MAI A. ; ...
Résumé
A systematic study was initiated of anode-supported solid oxide fuel cells (SOFCs) with Nd2NiO4 cathodes. This type of cathode, a mixed conducting K2NiF4-type material, can be considered as a candidate for SOFC applications. In this study, the influence of (I ) the presence of a Ce0.8Gd0.2O1.9 (CGO) interlayer between the electrolyte and the cathode, (2) sintering conditions, and (3) the grain size of the powder on the performance of SOFCs with Nd2NiO4 cathodes was investigated in more detail. Results from current density-voltage characteristics and permeation and gas diffusion measurements showed that the electrochemical performance was promising for SOFCs including a CGO interlayer and a Nd2NiO4 cathode (prepared with a powder with a d50 of 0.5 A/cm2 or 0.8 μm) sintered at 1100°C or higher; current density at 800°C and 700 mV between 1.2 and 1.3 A/cm2. The microstructure of the cathode was such that no gas diffusion problems occurred.
Editeur
ASME
Identifiant
ISSN : 1550-624X
Source
Journal of fuel cell science and technology A. 2009, vol. 6, n° 4, [041016.1-041016.6]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :