Correlation of thermal properties and electrical conductivity of La0.7Sr0.3Cu0.2Fe0.8O3-δ material for solid oxide fuel cells
Auteur(s)
WACKERL Jürgen ; KOPPITZ Thomas ; PECK Dong-Hyun ; ...
Résumé
A copper-doped ferrite with the chemical composition La0.7Sr0.3Cu0.2Fe0.s03-δ (LaSrCuFe) was prepared using the classical ceramics method starting from the oxides. The linear thermal expansion coefficient in air was measured in the temperature range between 550 and 1,250 K to be between 10 × 10―6 and 15 × 10―6 K―1. The electrical conductivity in air was found to be higher than 100 S cm―1 for temperatures lower than 1,100 K. A change of oxygen stoichiometry was found above 650 K in an atmosphere of 20 vol% oxygen with argon. This change can be correlated with the electrical conductivity.
Editeur
Springer
Identifiant
ISSN : 0021-891X CODEN : JAELBJ
Source
Journal of applied electrochemistry A. 2009, vol. 39, n° 8, pp. 1243-1249 [7 pages]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :