Détail de la notice
Titre du Document
Ti-doped isotropic graphite: A promising armour material for plasma-facing components
Auteur(s)
GARCIA-ROSALES C. ; LOPEZ-GALILEA I. ; ORDAS N. ; ...
Résumé
Finely dispersed Ti-doped isotropic graphites with 4 at.% Ti have been manufactured using synthetic mesophase pitch 'AR' as raw material. These new materials show a thermal conductivity at room temperature of ∼200 W/mK and flexural strength close to 100 MPa. Measurement of the total erosion yield by deuterium bombardment at ion energies and sample temperatures for which pure carbon shows maximum values, resulted in a reduction of at least a factor of 4, mainly due to dopant enrichment at the surface caused by preferential erosion of carbon. In addition, ITER relevant thermal shock loads were applied with an energetic electron beam at the JUDITH facility. The results demonstrated a significantly improved performance of Ti-doped graphite compared to pure graphite. Finally, Ti-doped graphite was successfully brazed to a CuCrZr block using a Mo interlayer. These results let assume that Ti-doped graphite can be a promising armour material for divertor plasma-facing components.
Editeur
Elsevier
Type du document
Conférence : International Conference on Fusion Reactor Materials (ICFRM), 13, Nice, FRA, 2007-12-10
Identifiant
ISSN : 0022-3115 CODEN : JNUMAM
Source
Journal of nuclear materials A. 2009, vol. 386-88, pp. 801-804 [4 pages] [bibl. : 17 ref.]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :