Selective Polishing of Polysilicon during Fabrication of Microelectromechanical Systems Devices
Auteur(s)
DANDU VEERA P. R. ; NATARAJAN A. ; HEGDE S. ; ...
Résumé
During a typical microelectromechanical systems device fabrication process, a polysilicon top layer has to be polished with a slurry that yields a high polysilicon removal rate (0.5 μm/min or more) and a high selectivity over the underlying silicon dioxide and silicon nitride layers (>50:1). In this work, polysilicon polish rates as high as 550 nm/min and selectivity over silicon dioxide and nitride of ― 130 and ― 260, respectively, have been achieved using colloidal silica and calcined ceria-based slurries containing arginine or lysine mono hydrochloride, at 4 psi down pressure. At 8 psi, polysilicon polish rates close to 900 nm/min and selectivities over both oxide and nitride that are close to 300 have been achieved. ξ potential, infrared spectroscopy, and contact angle data are used to explain the role of the amino acid additives in achieving the desired removal rate selectivities of polysilicon over silicon dioxide and silicon nitride.
Editeur
Electrochemical Society
Identifiant
ISSN : 0013-4651 CODEN : JESOAN
Source
Journal of the Electrochemical Society A. 2009, vol. 156, n° 6, [H487-H494]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :