Carbon nanotubes from ethanol on Fe-Co/MgO catalysts and related interface phenomena
Auteur(s)
LUPU D. ; BIRIS A. R. ; BALTOG I. ; ...
Résumé
Mossbauer spectroscopy studies of Fe-Co/MgO catalysts proved that a high dispersion degree of Fe may be achieved for catalysts containing Fe/Co in a ratio close to 1. During materials processing. the presence of hydrogen at high temperatures, even for short time, induced an increased particle size of the catalytic Fe. The evaluation of various iron species from their areas in the Mossbauer spectra revealed the dependence of the nanotube amount on (FeCo alloy + Fe2+) content in the catalyst, in good agreement with literature mechanisms. The Raman spectra show that carbon nanotubes synthesized from ethanol in argon flow on 4.5%Fe:4.5%Co/MgO are richer in low diameter (0.7-1.0nm) tubes than those obtained at low ethanol pressure, in agreement with the effects of hydrogen reported in literature. The close similarity with the Raman spectra of Aldrich double-walled carbon nanotubes and from literature, recommends the syntheses in argon flow as better conditions for double-walled carbon nanotube growth.
Editeur
INOE 2000
Identifiant
ISSN : 1454-4164
Source
Journal of optoelectronics and adavnced materials A. 2009, vol. 11, n° 3, pp. 338-347 [10 pages]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :