Surface area and thermal stability effect of the MgO supported catalysts for the synthesis of carbon nanotubes
Auteur(s)
YANG XU ; ZHONGRUI LI ; DERVISHI Enkeleda ; ...
Résumé
Surface area (SA) of the oxide support was found to play a major role on the morphology, quality of the single wall carbon nanotubes (SWNTs) growth. Fe-Co bimetal was supported onto MgO powders with different surface areas, and used for the SWNTs synthesis from the pyrolysis of CH4 through radio frequency catalytic chemical vapor deposition (RF-CCVD). The high surface area MgO showed specificity towards the growth of SWNTs even at the very high metal loadings of 17.4%. As the MgO surface areas decreased, the agglomeration of the active metal species on the support, nanotubes with wider diameter distributions and more graphitic walls were obtained. This surface area effect suggested that the high surface area networks were responsible for a more effective confinement of the active metal nanoparticles that impeded their migration during the SWNTs thermal growth process. Therefore, by adjusting the surface area or chemical morphology of the catalyst systems, SWNTs with narrower diameter distribution and specific chiralities can be grown.
Editeur
Royal Society of Chemistry
Identifiant
ISSN : 0959-9428
Source
Journal of material chemistry A. 2008, vol. 18, n° 47, pp. 5738-5745 [8 pages] [bibl. : 33 ref.]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :