Mechanical properties of polymer thin film measured by the bulge test
Auteur(s)
HUANG C. K. ; LOU W. M. ; TSAI C. J. ; ...
Résumé
The bulge test was used to measure the mechanical properties of polymer thin films with thickness in the range of 77 nm to 352 nm. The mechanical properties of polymeric thin films were extracted by comparing differences between curves of load vs. bulge height obtained from composite film configurations with and without the polymer layer. Both square and long rectangular windows were used to obtain the Poisson ratio and Young's Modulus. Composite film with 230 nm silicon nitride layer and 30 nm Al layer has a composite Poisson ratio of 0.29 and a Young's Modulus of 234+0.8 GPa. The Poisson ratio extracted for a 352 nm Poly(methyl methacrylate)-based thermoplastic polymeric thin film was 0.39. The Young's Modulus extracted for the 77 nm thick polymeric film is 4.9±0.8 GPa and for the 352 nm thick film is 5.8±0.2 GPa. In the thickness range investigated, no clear thickness dependence of the Young's modulus was observed using the Bulge test.
Editeur
Elsevier Science
Identifiant
ISSN : 0040-6090 CODEN : THSFAP
Source
Thin solid films A. 2007, vol. 515, n° 18, pp. 7222-7226 [5 pages] [bibl. : 22 ref.]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :