An EBSP study of isothermally-annealed cold-rolled nickel
Auteur(s)
BAKER I. ; LI J.
Résumé
Scanning electron microscopy and electron backscattered patterns, EBSP, have been employed to reveal both the grain structure and texture of 90% cold-rolled polycrystalline nickel after 1-hour anneals at a variety of temperatures. After annealing at either 400° or 500°C, small, cube-oriented, equi-axed grains were produced via primary recrystallization. At 600°C, large {124}<211> oriented grains accounted for an increasing proportion of the microstructure, until at 1000°C only large grains (∼600 μm) and a sharp {124}<211> texture were present. Detailed EBSP analyses of the grain boundaries surrounding the large abnormally grown grains observed at 600°C demonstrated that formation of the secondary recrystallization texture was due to migration of high-mobility, random high-angle boundaries around grains that had a size advantage, consistent with the Abbruzzese-Lücke model.
Editeur
Wiley-Liss
Identifiant
PMID : 15170759 ISSN : 1059-910X CODEN : MRTEEO
Source
Microscopy research and technique A. 2004, vol. 63, n° 5, pp. 289-297 [9 pages]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :