Titre du Document
Effect of polyvalent ion additions on the solarisation of annealed and toughened glass
Auteur(s)
CHIA D. ; CAUDLE B. ; ATKINS G. R. ; ...
Résumé
Solarisation of annealed and toughened sodium silicate glasses, and the effects of cerium and/or vanadium doping, were studied using radiation from a mercury lamp. In accordance with existing reports, pure sodium silicate glasses exhibited severe solarisation but addition of cerium to the glass was found to prevent solarisation. However, cerium doping may not suppress solarisation when other polyvalent elements are present; for example it was found that sodium silicate glasses doped with both cerium and vanadium suffered solarisation, with transmission losses of up to 8% at 500 nm. It was discovered that thermally toughened glasses, with compressive stress in the surface regions, are more susceptible to solarisation. An additional 2% transmission loss throughout the visible region was observed for all samples regardless of composition and assigned to absorption of ultraviolet (UV) light by point defects produced by the toughening process. This transmission loss may have important implications for the efficiency of solar panels protected by toughened glass.
Editeur
Society of Glass Technology
Identifiant
ISSN : 0017-1050 CODEN : GLSTAK
Source
Glass technology A. 2000, vol. 41, n° 5, pp. 165-168 [bibl. : 17 ref.]
Langue
Anglais
Pour les membres de la communauté du CNRS, ce document est autorisé à la reproduction à titre gratuit.
Pour les membres des communautés hors CNRS, la reproduction de ce document à titre onéreux sera fournie sous réserve d’autorisation du Centre Français d’exploitation du droit de Copie.

Pour bénéficier de nos services (strictement destinés aux membres de la communauté CNRS (Centre National de la Recherche Scientifique), de l'ESR français (Enseignement Supérieur et Recherche), et du secteur public français & étranger) :